Gray Cast Iron Magnetic Properties

Gray Iron Paghahambing				Microstructure（Volume Fractions）（％）
China（GB/T 9439)	ISO 185	ASTM A48/A48M	EN 1561	Istraktura ng Matrix
HT100 (HT10-26)	100	No.20 F11401	EN-GJL-100	Pearlite: 30-70％, magaspang na mga natuklap; Ferrite: 30-70％; Binary Phosphorus Eutectic: ＜7％
HT150 (HT15-33)	150	No.25A F11701	EN-GJL-150	Pearlite: 40-90％, medium coarse flakes; Ferrite: 10-60％; Binary Phosphorus Eutectic:＜7％
HT200 (HT20-40)	200	No.30A F12101	EN-GJL-200	Pearlite: ＞95％, medium flakes; Ferrite＜5％; Binary Phosphorus Eutectic＜4％
HT250 (HT25-47)	250	No.35A F12401 No.40A F12801	EN-GJL-250	Pearlite: ＞98％ medium thin flakes; Binary Phosphorus Eutectic:＜2％
HT300 (HT30-54)	300	No.45A F13301	EN-GJL-300	Pearlite: ＞98％ medium thin flakes; Binary Phosphorus Eutectic:＜2％
HT350 (HT35-61)	350	No.50A F13501	EN-GJL-350	Pearlite: ＞98％ medium thin flakes; Binary Phosphorus Eutectic: ＜1％

 

Ang mga magnetic na katangian ng gray cast iron ay malawak na nag-iiba, mula sa mababang permeability at high coercive force hanggang sa high permeability at low coercive force. Ang mga pagbabagong ito ay pangunahing nakadepende sa microstructure ng gray cast iron. Ang pagdaragdag ng mga elemento ng alloying upang makuha ang kinakailangang magnetic properties ay nakakamit sa pamamagitan ng pagbabago ng istraktura ng gray cast iron.

Ang Ferrite ay may mataas na magnetic permeability at mababang hysteresis loss; Ang pearlite ay kabaligtaran lamang, ito ay may mababang magnetic permeability at malaking pagkawala ng hysteresis. Ang Pearlite ay nabuo sa ferrite sa pamamagitan ng pagsusubo ng init na paggamot, na maaaring mapataas ang magnetic permeability ng apat na beses. Ang pagpapalaki ng mga butil ng ferrite ay maaaring mabawasan ang pagkawala ng hysteresis. Ang pagkakaroon ng cementite ay magbabawas ng magnetic flux density, permeability at remanence, habang pinapataas ang permeability at hysteresis loss. Ang pagkakaroon ng magaspang na grapayt ay magbabawas sa remanence. Ang pagbabago mula sa A-type graphite (isang flake-shaped graphite na pantay na ipinamamahagi nang walang direksyon) sa isang D-type na graphite (isang pinong kulot na graphite na may di-directional distribution sa pagitan ng mga dendrite) ay maaaring makabuluhang tumaas ang magnetic induction at coercive force .

Bago maabot ang non-magnetic na kritikal na temperatura, ang pagtaas ng temperatura ay makabuluhang pinatataas ang magnetic permeability ng gray cast iron. Ang Curie point ng purong bakal ay ang α-γ transition temperature na 770°C. Kapag ang mass percentage ng silicon ay 5%, ang Curie point ay aabot sa 730°C. Ang Curie point temperature ng cementite na walang silicon ay 205-220°C.

Ang istraktura ng matrix ng mga karaniwang ginagamit na grado ng gray cast iron ay pangunahing perlite, at ang kanilang maximum na permeability ay nasa pagitan ng 309-400 μH/m.

 

Mga Magnetic na Katangian ng Gray Cast Iron
Code ng Gray Iron	Komposisyon ng kemikal (%)
	C	Si	Mn	S	P	Ni	Cr
A	3.12	2.22	0.67	0.067	0.13	<0.03	0.04
B	3.30	2.04	0.52	0.065	1.03	0.34	0.25
C	3.34	0.83 - 0.91	0.20 - 0.33	0.021 - 0.038	0.025 - 0.048	0.04	<0.02
Magnetic na Katangian		A		B		C
		Pearlite	Ferrite	Pearlite	Ferrite	Pearlite	Ferrite
Carbide Carbon w(%)		0.70	0.06	0.77	0.11	0.88	/
Remanence / T		0.413	0.435	0.492	0.439	0.5215	0.6185
Puwersang Puwersa / A•m-1		557	199	716	279	637	199
Pagkawala ng Hysteresis / J•m-3•Hz-1 (B=1T)		2696	-696	2729	1193	2645	938
Lakas ng Magnetic Field / kA•m-1 (B=1T)		15.9	-5.9	8.7	8.0	6.2	4.4
Max. Magnetic Permeability / μH•m-1		396	1960	353	955	400	1703
Lakas ng Magnetic Field kapag Max. Magnetic Permeability / A•m-1		637	199	1035	318	1114	239
Resistivity / μΩ•m		0.73	0.71	0.77	0.75	0.42	0.37

 

Narito sa mga sumusunod ang mga mekanikal na katangian ng grey cast iron:

Mga Mechanical na Katangian ng Gray Cast Iron
Item ayon sa DIN EN 1561	Sukatin	Yunit	EN-GJL-150	EN-GJL-200	EN-GJL-250	EN-GJL-300	EN-GJL-350
			EN-JL 1020	EN-JL 1030	EN-JL 1040	EN-JL 1050	EN-JL 1060
Lakas ng makunat	Rm	MPA	150-250	200-300	250-350	300-400	350-450
0.1% Lakas ng Yield	Rp0,1	MPA	98-165	130-195	165-228	195-260	228-285
Lakas ng pagpahaba	A	%	0,3 – 0,8	0,3 – 0,8	0,3 – 0,8	0,3 – 0,8	0,3 – 0,8
Lakas ng Compressive	σdB	MPa	600	720	840	960	1080
0,1% Lakas ng Compressive	σd0,1	MPa	195	260	325	390	455
Flexural na Lakas	σbB	MPa	250	290	340	390	490
Schuifspanning	σaB	MPa	170	230	290	345	400
Shear Stress	TtB	MPa	170	230	290	345	400
Mga module ng pagkalastiko	E	GPa	78 – 103	88 – 113	103 – 118	108 – 137	123 – 143
Numero ng Poisson	v	–	0,26	0,26	0,26	0,26	0,26
Katigasan ng Brinell		HB	160 – 190	180 – 220	190 – 230	200 – 240	210 – 250
Kalusugan	σbW	MPa	70	90	120	140	145
Pagbabago ng tensyon at presyon	σzdW	MPa	40	50	60	75	85
Lakas ng Pagsira	Klc	N/mm3/2	320	400	480	560	650
Densidad		g/cm3	7,10	7,15	7,20	7,25	7,30